Large Fire Brick Refractory Castable For Glass Furnace Bottom And Wall
Castable refractory cement is a premium castable refractory material designed for industrial applications that require high-temperature resistance and structural integrity. Engineered to withstand extreme heat, mechanical stress, and chemical corrosion, this material is widely used in furnaces, kilns, and thermal equipment.
This castable refractory cement, as a high-quality castable refractory material, combines ease of application, heat resistance, and long-lasting durability. It is ideal for industrial operations requiring robust, reliable, and high-temperature refractory solutions.
This versatile castable refractory is easy to mix, pour, and mold, providing seamless linings for various high-temperature environments. It offers exceptional durability, excellent bonding properties, and minimal shrinkage, making it a reliable choice for long-term refractory performance.
Description:
Using big vibrating table and adopting special castables, the company produces furnace large fireclay blocks with vibrate moulding technology. The physical and chemical properties and appearance of the blocks have exceeded the national standards. The resistant ability to molten glass of the products is better than that of fanditional casting process products and ramming products . the products are especially suitable to build the bottom of furnace, cooling and working end side wall of glass furnace.
The most competitive price,good quality,safty packing,prompt delivery time,and excellent after-sales services.
Lower ferric Oxide,lower porosity,higher refractoriness,higher density,higher CCS and exact tolerance.
Features:
1. Move Cast shaped
2. Excellent corrosion resistant of glass liquid.
3. can resist high temperature
Applications:
Used for glass furnace bottom and wall and so on
Specifications:
Technical data
| Item | Index | |
| LA-40a | LA-40b | |
| Al2O3 ,% ≥ | 40 | |
| Fe2O3 ,% ≤ | 1.5 | 1.8 |
| 0.2Mpa refractoriness under load , ℃ ≥ | 1450 | 1400 |
| Linear change after reheating %1400℃,2h | 0 | |
| Apparent porosity,% ≤ | 18 | 18 |
| Compress strength, Mpa ≥ | 49 | 35 |
| Density,g/cm3 | 2.3 | 2.3 |