Hight quality anti-slip water permeable bricks for walking and
This product uses the slag waste, waste ceramics as raw material.
After re-processing, high temperature sintering, the environmental
product is produced with characteristics of keeping the ground
water permeability, preserving moisture, compression-resistant,
slip-proof, high strength, cold resistance, weather resistance,
noise reduction, sound absorption and reusability.
Water permeable ceramic bricks are the preferred products used to
beautify the city, improve the quality of living environment, and
can be widely used in the building of public of public squares,
city road, subway, station, highway, villas, residential quarters,
parks, landscape, garden decoration, kitchen space, swimming pool
1. Water retention
---It can be used to reduce the temperature of the environment,
restore natural water storage capacity, prevent the depletion of
groundwater, and improve the living environment of vegetation. It
can adjust the air humidity, air purification, and restore surface
water circulation system.
---Rainwater infiltrates into the ground timely. There is no water.
It keeps the ground dry and clean. Walking on it brings no danger.
---The porous structure of the ecological permeable ceramic bricks
can absorb a large amount of noise. It is an ideal sound-absorbing
---The ecological permeable ceramic bricks can be reused again and
easy to re-install. It prevents waste from repetitive
5. Compression resistant, cold resistant, weathering resistant
---The ecological permeable ceramic bricks are made undergone the
large tonnage pressing machine and high temperature firing. The
compressive strength is ≥50Mpa, suitable for use in the parking
lots and common lanes. Its cold-resistance also reached the
national standard, and frost resistance value is -25℃. It is also
resistant to weathering, even in the face of strong acid or alkali.
Its quality will not change, and it is most suitable for seaport
|Inspection Items||Standard Values||Test Value|
|Compressive Strength (Mpa )||≥35||≥50|
|Breaking Strength (Mpa )||≥3.5||≥6.0|
|Permeability Coefficient (CM/S)||≥2.0* 0.01||≥3.0* 0.01|
|Skid resistance (BPM)||≥60||≥70|